Industries supplied include: appliances, kitchen utensils, tank covers, and other deep drawn parts. 305 grade stainless has similar corrosion resistance as 304 and has good oxidation resistance in air up to 1650 F (899 C). 305 can be readily formed and deep drawn into complex shapes due to its lower strength and work hardening rate and will remain nonmagnetic after cold work unlike 301 or 304. A caution is autogenous welds in 305 are more sensitive to hot cracking than 304 or 304L.
17.0 – 19.0
10.0 – 13.0
Physical Properties At 70°F (At 20°C)
0.29 lb./in3 / (7.99 g/cm3)
Modulus of Elasticity (E)
28.0 x 103 ksi / (193 x 103MPa)
Coefficient of Expansion
9.6 x 10-6 microinches/in.-°F (32-212°F) / (17.3 μm/m-°C) (0-100°C)
28.4 μ ohm.in / (72 μ ohm.cm)
9.4 Btu-in./ft.2hr.-°F (100°C)/ (16.2 W/m-K (100°C))
AMS 5514, ASTM A240
Typical Mechanical Properties – Typical Room Temperature Mechanical Properties
Tensile Strength Min (UTS)
85 ksi (586 MPa)
0.2% YS Min
35 ksi (241 MPa)
Elongation% in 2” Min (50.8 mm)
70 HRBW (Max)
*The information and data in this product data sheet are accurate to the best of our knowledge and belief, but are intended for general information only. Applications suggested for the materials are described only to help readers make their own evaluations and decisions, and are neither guarantees nor to be construed as express or implied warranties of suitability for these or other applications. Data was obtained from our melt sources with data referring to mechanical properties and chemical analyses are the result of tests performed on specimens obtained from specific locations with prescribed sampling procedures; any warranty thereof is limited to the values obtained at such locations and by such procedures. There is no warranty with respect to values of the materials at other locations. Further information should be sought from the melt sources.
Additional Information on 305 Stainless Steel
We produce all of our stainless steel using the highest quality processes and materials. Our aim is to provide you with high quality metal that is competitively priced, carefully packaged, and delivered in spec and on time. One such high quality item is type 305 stainless steel, which we will go into detail on after first considering the primary types of stainless steel.
Properties of Type 305 Stainless Steel
Stainless Steel type 305 is an austenitic Chromium-Nickel alloy with a low rate of work hardening that makes it a good choice for many deep drawing applications. When ordering 305 stainless steel, note the deep drawing quality. Ordering annealed or dead soft will not guarantee this however. This alloy is non-magnetic but will slowly become so with increasing cold work.
Processing & Forming of 305 Stainless Steel
Type 305 is an austenitic, Chromium-Nickel stainless steel alloy with an increased Nickel content that allows it to be spun and deep drawn easily while decreasing work hardening. Stainless steel 305 cannot be hardened by heat treatment.
Unlike Type 301 and 304, Type 305 stainless steel remains non-magnetic after cold work. It can be readily formed and deep drawn into complex shapes due to its lower strength and hardening rates. It is used for a wide variety of products in the chemical, textile, petroleum, dairy, and food industries.