Alloy 410S Stainless Steel

Alloy 410S Stainless Steel

Alloy 410S Stainless Steel Chemical Analysis The austenitic stainless steels are considered to be the most weldable of the high-alloy steels and can be welded by all fusion and resistance welding processes. *Alloy predominates remaining composition. Other elements may be present only in minimal...
Chat Now

Product Details

Alloy 410S Stainless Steel

Chemical Analysis

The austenitic stainless steels are considered to be the most weldable of the high-alloy steels and can be welded by all fusion and resistance welding processes.





Chromium11.5 min.-14.5 max.Sulfer.030 max.
Nickel0.60 max.Silicon1.00 max.
Carbon0.08 max.IronBalance*
Manganese1.00 max.Phosphorus0.040 max.

*Alloy predominates remaining composition. Other elements may be present only in minimal quantities.


Physical Properties

Density

0.28 lbs/in3
7.73 g/cm3

Magnetic Permeability

0.28 lb/in3
7.73 g/cm3

Specific Heat

0.11 BTU/lb-°F (32 – 212°F)
0.46 J/kg-°K (0 – 100°C)

Modulus of Elasticity

29 x 106 psi
200 GPa

Thermal Conductivity 212°F (100°C)

187 BTU/hr/ft2/ft/°F
26.9 W/m-°K

Melting Range

2700 – 2790°F
1480 – 1530°C

Electrical Resistivity

23.7 Microhm-in at 68°C
60 Microhm-cm at 20°C


Linear Coefficient of Thermal Expansion


In/in°Fum/m-°K
32 - 212°F (0 - 100°C)6.0 x 10-610.8
32 - 600°F (0 - 315°C)6.4 x 10-611.5
32 - 1000°F (0 - 538°C)6.7 x 10-612.2
32 - 1200°F (0 - 649°C)7.5 x 10-613.5


Mechanical Properties

Typical Room Temperature Mechanical Properties, Mill Annealed

Yield Strength
0.2% Offset
Ultimate Tensile
Strength
Elongation
in 2 in.%
Hardness
Rockwell B
Reduction
percent of area


psi(MPa)psi(MPa)


42,00029064,400444337565