General Characteristics
201/4618 is an austenitic stainless steel, which belongs to the austenitic low-nickel CrMn stainless steel family, in which manganese replaces part of the nickel that is normally alloyed to CrNi standard grades. This variant has low nitrogen content and copper alloying for improved forming properties.
Corrosion resistance of the austenitic CrMn grades is usually slightly below that of the austenitic CrNi standard grades. 201/4618 is used in applications where good formability and corrosion resistance are needed.
Typical Applications
Household appliances & consumer goods
Kitchen utensils
Tableware
Cutlery
Pots & pans
Sinks & countertops
Indoor cladding
Window frames
Automotive applications
Product forms, available sizes and finishes
Flat
Product type | Finishes | Thickness | Width |
Cold rolled coil | 2B, 2BB, 2C, 2D, 2E, 2G, 2J, 2R | 0,05-3,00 | 3-1530 |
Cold rolled sheet | 2B, 2BB, 2D, 2E, 2G, 2J, 2R | 0,40-3,00 | 600-1530 |
Hot rolled coil, pickled | 1C, 1D, 1G, 1U | 2,00-8,00 | 50-1550 |
Precision strip | 2R | 0,05-1,50 | 3-649 |
Chemical Composition
The typical chemical composition for this grade is given in the table below, together with composition limits given for the product according to different standards. The required standard will be fully met as specified on the order.
The chemical composition is given as % by mass.
C | Mn | Cr | Ni | N | Other | |
Typical | 0.06 | 7.9 | 16.6 | 4.6 | Cu:1.7 | |
EN 10088-2 | ≤0.10 | 5.5-9.5 | 16.5-18.5 | 4.5-5.5 | ≤0.15 | Cu:1.00-2.50 |
Mechanical Properties
Standard | Rp0.2 | Rp1.0 | Rm | Elongation |
MPa | MPa | MPa | % | |
Product type: Cold rolled coil and sheet | ||||
Typical (thickness 1 mm) | 310 | 335 | 640 | |
EN 10088-2 | ≥ 230 | ≥ 250 | 540-850 | ≥ 45 |
Product type: Hot rolled coil and sheet | ||||
EN 10088-2 | ≥ 230 | |||
Product type: Hot rolled quarto plate | ||||
EN 10088-2 | ≥ 210 | ≥ 240 | 520-830 | ≥ 45 |
Physical Properties
Density | Modulus of elasticity | Thermal exp. at 100 °C | Thermal conductivity |
kg/dm3 | GPa | 10-6/°C | W/m°C |
7,9 | 200 | 16,0 | 15 |