Specific Weight of Hot Rolled 25mm Thick Stainless Steel 304 Plate
Stainless steel 304 also known as 1.4301 respectively. Type 304 is the most versatile and widely used stainless steel.
It is still sometimes referred to by its old name 18/8 which is derived from the nominal composition of type 304 being 18% chromium and 8% nickel.
Chemical Compositions
% Present | |
Carbon (C) | 0.07 |
Chromium (Cr) | 17.50 - 19.50 |
Manganese (Mn) | 2.00 |
Silicon (Si) | 1.00 |
Phosphorous (P) | 0.045 |
Sulphur (S) | 0.015b) |
Nickel (Ni) | 8.00 - 10.50 |
Nitrogen (N) | 0.10 |
Iron (Fe) | Balance |
Mechanical properties
Property | Value |
Comprehensive Strength | 210 MPa |
Proof Stress | 210 Min MPa |
Tensile Strength | 520 - 720 MPa |
Elongation | 45 Min% |
Physical Properties
Property | Value |
Density | 8,000 Kg/m3 |
Melting Point | 1450 °C |
Thermal Expansion | 17.2 x 10-6 /K |
Modulus of Elasticity | 193 GPa |
Thermal Conductivity | 16.2W/m.K |
Electrical Resistivity | 0.072 x 10-6 Ω .m |