This data sheet applies to stainless steel 430 / 1.4016 hot and cold-rolled sheets/plates and strips, semi-finished products, rods, wire, sections and bright products for general purpose.
Application
Rail and road vehicles, container building, warehouse and transport devices for the sugar industry, sound absorber, coal mining. The steel is resistant to intergranular corrosion.
Chemical Compositions
| Element | % Present (in product form) | |
| C, H, P | L | |
Carbon (C) | ≤0.08 | ≤0.08 |
Silicon (Si) | ≤1.00 | ≤1.00 |
Manganese (Mn) | ≤1.00 | ≤1.00 |
Phosphorous (P) | ≤0.040 | ≤0.040 |
Sulfur (S) | ≤0.015 | ≤0.030 |
Chromium (Cr) | 16.00 - 18.00 | 16.00 - 18.00 |
Iron (Fe) | Balance | Balance |
Mechanical properties (at room temperature in annealed condition)
| Product Form | Thickness t or diameter4) d mm max | Yield Strength Rp0.2 | Tensile Strength | Elongation min. in % | |
| N/mm2 (longitudinal) | N/mm2 (transverse) | Rm N/mm2 | A80mm1) ˂3mm thickness (longitudinal and transverse) | ||
| C | 8 | 260 | 280 | 450 - 600 | 20 |
H | 13.5 | 240 | 260 | 450 - 600 | 18 |
P | 25 | 240 | 260 | 430 - 630 | 20 |
L | 100 | 240 | - | 400 - 630 | 20 (longitudinal) |
Minimum values of the 0.2 %-Yield strength of ferritic steels at elevated temperatures
| Product | Heat Treatment Condition | 0.2 %-Yield strength at the temperature °C | ||||||
| 100 | 150 | 200 | 250 | 300 | 350 | 400 | ||
| C, H, P, L | Annealed | 220 | 215 | 210 | 205 | 200 | 195 | 190 |
Reference data on some physical properties
| Density at 20°C kg/m3 | 7,700 | |
| Modulus of Elasticity kN/mm2 at | 20°C | 220 |
200°C | 210 | |
400°C | 195 | |
500°C | - | |
Thermal Conductivity W/m K at 20°C | 25 | |
Specific Thermal Capacity at 20°C J/kg K | 460 | |
Electrical Resistivity at 20°C Ω mm2 /m | 0.60 | |