Introduce 201 Grade
Type 201 is an austenitic chromium-nickel manganese stainless steel that was developed originally
to conserve nickel. It provides properties similar to Type 301 and can be used in most applications for
Type 301. This alloy is non-magnetic in the annealed condition, but becomes magnetic whencold worked.
The rate of work hardening is similar to Type 301, although Type 201 develops somewhat higher
yield strength while retaining equal ductility when cold worked. Toughness at low temperatures is excellent.
Typical uses include appliances, restaurant equipment,cooking utensils, sinks, automotive trim,
architectural applications such as windows and doors, railway cars, trailers and hose clamps.
SUS 201 Stainless Steel Sheet
Standard: ASTM A240/A480, JIS G4305/G4304, EN 10088-2
Surface: No.1, 2B, BA, No.3, No.4, No.6, HL, No.8, SB
Colour: Golden mirror, Rose Golden mirror, Yellow Titanium, black and so on
Sheet/plate/coil/strip Thickness: 0.02 ~ 5.0 mm (CR), 3.0 ~ 120.0 mm (HR)
Sheet/plate/coil/strip Width: 4.0 ~ 2,000 mm(CR), 50-3,300mm(HR)
SUS 201 Stainless Steel Sheet | ||||||||
Grade | Chemical composition | |||||||
C | Si | Mn | P | S | Ni | N | Cr | |
% | % | % | % | % | % | % | % | |
201 | ≤0.15 | ≤1.0 | 5.5~7.50 | ≤0.060 | ≤0.030 | 3.50~5.50 | ≤0.2 | 13.50-16.00 |
| Hardness | Tensile Strength | Yield Strength | Elongation | Reduction in area | density | Recommended heat treatment |
HRB | Mpa | Mpa | % | % | kg/m³ | °C |
≤100 | ≥520 | ≥205 | ≥40 | ≥50 | 7.93 | 1030-1180 |